Grade
|
C (Max)
|
Mn (Max)
|
P (Max)
|
S (Max)
|
Si (Max)
|
Cr
|
Ni
|
Mo
|
Nitrogen (Max)
|
Cu/ Others
|
301
|
0.15
|
2.00
|
0.045
|
0.030
|
1.00
|
16.00 – 18.00
|
6.00 – 8.00
|
-
|
0.10
|
-
|
304
|
0.08
|
2.00
|
0.045
|
0.030
|
0.75
|
18.00 – 20.00
|
8.00- 10.50
|
-
|
0.10
|
-
|
304L
|
0.030
|
2.00
|
0.045
|
0.030
|
0.75
|
18.00 – 20.00
|
8.00- 12.00
|
-
|
0.10
|
-
|
310S
|
0.08
|
2.00
|
0.045
|
0.030
|
1.50
|
24.00- 26.00
|
19.00 – 22.00
|
-
|
-
|
-
|
316
|
0.08
|
2.00
|
0.045
|
0.030
|
0.75
|
16.00 – 18.00
|
10.00 – 14.00
|
2.00 – 3.00
|
0.10
|
-
|
316L
|
0.030
|
2.00
|
0.045
|
0.030
|
0.75
|
16.00 – 18.00
|
10.00 – 14.00
|
2.00 – 3.00
|
0.10
|
-
|
317
|
0.08
|
2.00
|
0.045
|
0.030
|
0.75
|
18.00 – 20.00
|
11.00 – 14.00
|
3.00 – 4.00
|
0.10
|
-
|
317L
|
0.030
|
2.00
|
0.045
|
0.030
|
0.75
|
18.00 – 20.00
|
11.00 – 15.00
|
3.00 – 4.00
|
0.10
|
-
|
321
|
0.08
|
2.00
|
0.045
|
0.030
|
0.75
|
17.00 – 19.00
|
9.00 – 12.00
|
-
|
0.10
|
Ti5 ( C + N ) Min or 0.70 max
|
347
|
0.08
|
2.00
|
0.045
|
0.030
|
0.75
|
17.00 – 19.00
|
9.00 – 13.00
|
-
|
-
|
Cb= 10x ( C Min ) or 1.00 Max
|
409
|
0.08
|
1.00
|
0.040
|
0.010
|
1.00
|
10.50 – 11.75
|
0.50
|
-
|
-
|
Ti= 6x (C+ N ) Min or 0.70 Max
|
409M
|
0.03
|
0.81.2
|
0.030
|
0.030
|
0.40.75
|
11.00- 12.00
|
1.5 max.
|
-
|
-
|
Ti= 6x (C) Min or 0.70 Max
|
410S
|
0.08
|
1.00
|
0.040
|
0.030
|
1.00
|
11.50- 13.50
|
0.60
|
-
|
-
|
-
|
410
|
0.15
|
1.00
|
0.040
|
0.030
|
1.00
|
11.50- 13.50
|
0.75
|
-
|
-
|
-
|
420
|
0.35
|
0.50
|
0.035
|
0.015
|
0.50
|
12.00 – 13.00
|
0.20.3
|
-
|
-
|
-
|
430
|
0.12
|
1.00
|
0.040
|
0.030
|
1.00
|
16.00 – 18.00
|
0.75
|
-
|
-
|
-
|
JSL AUS
|
0.08
|
7.08.0
|
0.070
|
0.030
|
0.75
|
15.50 – 16.50
|
4.25 – 4.75
|
-
|
-
|
0.9 – 1.10
|
JS- 203
|
0.08
|
9.2510.25
|
0.070
|
0.030
|
0.75
|
14.25 – 15.25
|
2.25 – 2.75
|
-
|
-
|
1.60- 2.0
|
301M
|
0.10
|
4.55.5
|
0.060
|
0.030
|
0.75
|
14.50 – 15.50
|
6.0 – 7.0
|
-
|
-
|
1.70- 1.90
|
* Thickness of 1.27mm & below will have elongation of 20% min.
|
Chemical Composition,% |
Tensile Test |
|||||||
Designation
|
C max.
|
Si
|
P max
|
S max
|
Tensile Strength Kgf/mm2
|
Yield Point Kgf/mm2,min.
|
Elongation
|
|
Test Piece
|
%, min
|
|||||||
IS 2002-1
|
0.18
|
.010-0.35
|
0.40
|
0.40
|
37-45
|
55
|
5.65/So
4/So |
26
30 |
IS 2002-2A
|
0.20
|
0.10-0.35
|
0.050
|
0.050
|
42-50
|
50
|
5.65/So
4/So |
25
29 |
IS 2002-2b
|
0.22
|
0.10-0.35
|
0.050
|
0.050
|
52-62
|
50
|
5.65/So
4/So |
20
24 |
Chemical Composition,%
|
Tensile Test |
Bend test |
|||
Designation
|
C Si Mn P S
Max Max Max |
Yield Point Tensile Strength
Kgf/mm2 Kgf/mm2.(N/mm2) |
Elongation
%, Test Piece |
Angle of Bend
|
Inside Radius
|
AG
|
0.09 tr.0.20-0.40 0.30 0.030
|
– –
|
– –
|
Chemical Composition,%
|
Tensile Test*1 |
1. (i) Refer to (1) for ASTM A 203 (ii) Refer to (2) for ASTM A 203 (iii) Refer to (4) for ASTM A 203. |
|||||||
Designation
|
C max
|
Mn max
|
P max
|
S max
|
Tensile Strength
ksi (MPa), |
Yeild Strengh ksi(MPa),min.
|
Elongation,% min
|
||
GL=8 in. |
|||||||||
A 285 A
|
0.17
|
0.90
|
0.035
|
0.040
|
45-65 (310-450)
|
24(165)
|
27 30
|
||
A 285 B
|
0.22
|
0.90
|
0.035
|
0.040
|
50-70(385-485)
|
27(185)
|
25
28 |
||
A 285 C
|
0.28
|
0.90
|
0.035
|
0.040
|
55-75(380-515)
|
30(205)
|
23 27
|
Grade
|
Tensile
Strength Mpa, (Min) |
Yield
Strength Mpa, (Min) |
%Age
Elongation in 50mm gauge length min |
Hardness (Max)
|
|
BHN
|
Rb
|
||||
301
|
515
|
205
|
40
|
217
|
95
|
304
|
515
|
205
|
40
|
201
|
92
|
304L
|
485
|
170
|
40
|
201
|
92
|
310S
|
515
|
205
|
40
|
217
|
95
|
316
|
515
|
205
|
40
|
217
|
95
|
316L
|
485
|
170
|
40
|
217
|
95
|
317
|
515
|
205
|
35
|
217
|
95
|
317L
|
515
|
205
|
40
|
217
|
95
|
321
|
515
|
205
|
40
|
217
|
95
|
347
|
515
|
205
|
40
|
201
|
92
|
409
|
380
|
170
|
20
|
179
|
88
|
409M
|
430
|
275
|
20
|
187
|
90
|
410S
|
415
|
205
|
22
|
183
|
89
|
410
|
450
|
205
|
20
|
217
|
89
|
420
|
700( max )
|
-
|
15
|
217
|
95
|
430
|
450
|
205
|
22
|
183
|
89
|
JSL AUS
|
515
|
205
|
40
|
217
|
95
|
JS- 203
|
515
|
205
|
40
|
217
|
95
|
301M
|
515
|
205
|
40
|
217
|
95
|
Chemical Composition,% |
Tensile Test |
|||||||
Designation
|
C max.
|
Si
|
P max
|
S max
|
Tensile Strength Kgf/mm2
|
Yield Point Kgf/mm2,min.
|
Elongation
|
|
Test Piece
|
%, min
|
|||||||
IS 2002-1
|
0.18
|
.010-0.35
|
0.40
|
0.40
|
37-45
|
55
|
5.65/So
4/So |
26
30 |
IS 2002-2A
|
0.20
|
0.10-0.35
|
0.050
|
0.050
|
42-50
|
50
|
5.65/So
4/So |
25
29 |
IS 2002-2b
|
0.22
|
0.10-0.35
|
0.050
|
0.050
|
52-62
|
50
|
5.65/So
4/So |
20
24 |
Nominal Broe
|
Outside Diameter
|
Schedule 5S
|
Schedule 10S
|
Schedule 40S
|
Schedule 80S
|
Schedule 160S
|
Schedule XXS
|
|||||||
mm
|
INCH
|
mm
|
Wt mm
|
Weight (Kg/mt)
|
Wt
mm |
Weight (Kg/mt)
|
Wt
mm |
Weight (Kg/mt)
|
Wt
mm |
Weight (Kg/mt)
|
Wt mm
|
Weight (Kg/mt)
|
Wt
mm |
Weight (Kg/mt)
|
3
|
1/8
|
10.3
|
1.24
|
0.276
|
1.24
|
028
|
1.73
|
0.37
|
2.41
|
0.47
|
-
|
-
|
-
|
-
|
6
|
1/4
|
13.7
|
1.24
|
0.390
|
1.65
|
049
|
2.24
|
0.631
|
3.02
|
.0.80
|
-
|
-
|
-
|
-
|
10
|
3/8
|
17.1
|
1.24
|
0.490
|
1.65
|
0.63
|
2.31
|
0.845
|
3.20
|
1.10
|
-
|
-
|
-
|
-
|
15
|
1/2
|
21.3
|
1.65
|
0.800
|
2.11
|
1.00
|
2.77
|
1.27
|
3.75
|
1.62
|
4.75
|
1.94
|
7.47
|
2.55
|
20
|
3/4
|
26.7
|
1.65
|
1.03
|
2.11
|
1.28
|
2.87
|
1.68
|
3.91
|
2.20
|
5.54
|
2.89
|
7.82
|
3.63
|
25
|
1
|
33.4
|
1.65
|
1.30
|
2.77
|
2.09
|
3.38
|
2.50
|
4.55
|
3.20
|
6.35
|
4.24
|
9.09
|
5.45
|
32
|
1.1/4
|
42.2
|
1.65
|
1.65
|
2.77
|
2.70
|
3.56
|
3.38
|
4.85
|
4.47
|
6.35
|
5.61
|
9.70
|
7.77
|
40
|
1.1/2
|
48.3
|
1.65
|
1.91
|
2.77
|
3.11
|
3.68
|
4.05
|
5.08
|
5.41
|
7.14
|
7.25
|
10.16
|
9.54
|
50
|
2
|
60.3
|
1.65
|
2.40
|
2.77
|
3.93
|
3.91
|
5.44
|
5.54
|
7.48
|
8.74
|
11.1
|
11.07
|
13.44
|
65
|
2.1/2
|
73.0
|
2.11
|
3.69
|
3.05
|
5.26
|
5.16
|
8.63
|
7.01
|
11.4
|
9.53
|
14.9
|
14.2
|
20.39
|
80
|
3
|
88.9
|
2.11
|
4.51
|
3.05
|
6.45
|
5.49
|
11.30
|
7.62
|
15.2
|
11.1
|
21.3
|
15.24
|
27.65
|
100
|
4
|
114.3
|
2.11
|
5.84
|
3.05
|
8.36
|
6.02
|
16.07
|
8.56
|
22.3
|
13.49
|
33.54
|
17.12
|
41.03
|
125
|
5
|
141.3
|
2.77
|
9.47
|
3.40
|
11.57
|
6.55
|
21.8
|
9.53
|
31.97
|
15.88
|
49.11
|
19.05
|
57.43
|
150
|
6
|
168.3
|
2.77
|
11.32
|
3.40
|
13.84
|
7.11
|
28.3
|
10.97
|
42.7
|
18.2
|
67.56
|
21.95
|
79.22
|
200
|
8
|
219.1
|
2.77
|
14.79
|
3.76
|
19.96
|
8.18
|
42.6
|
12.7
|
64.6
|
23.0
|
111.2
|
22.23
|
107.8
|
250
|
10
|
273.1
|
3.40
|
22.63
|
4.19
|
27.78
|
9.27
|
60.5
|
12.7
|
96.0
|
28.6
|
172.4
|
25.40
|
155.15
|
300
|
12
|
323.9
|
3.96
|
31.25
|
4.57
|
36.00
|
9.52
|
73.88
|
12.7
|
132.0
|
33.32
|
238.76
|
25.40
|
186.97
|
350
|
14
|
355.6
|
3.96
|
34.36
|
4.78
|
41.3
|
11.13
|
94.59
|
19.05
|
158.08
|
35.71
|
281.70
|
-
|
-
|
400
|
16
|
406.4
|
4.19
|
41.56
|
4.78
|
47.29
|
12.7
|
123.30
|
21.41
|
203.33
|
40.46
|
365.11
|
-
|
-
|
450
|
18
|
457.2
|
4.19
|
46.80
|
4.78
|
53.42
|
14.27
|
155.80
|
23.8
|
254.36
|
45.71
|
466.40
|
-
|
-
|
500
|
20
|
508.0
|
4.78
|
59.25
|
5.54
|
68.71
|
15.09
|
183.42
|
26.19
|
311.2
|
49.99
|
564.68
|
-
|
-
|
600
|
24
|
609.6
|
5.54
|
82.47
|
6.35
|
94.45
|
17.48
|
255.41
|
30.96
|
442.08
|
59.54
|
808.22
|
-
|
-
|